EGM-100 epoxy grout EGM-100 epoxy grout material comprises A (resin), B (hardener), C (filler) three-component, the product of high quality and refined resin filler, 100% solids, It does not contain harmful solvents and other volatile substances. At room temperature will be using a three-component material contained in each thoroughly mixed after without adding additional ingredients. First, the product features 1, high strength, early strength: it can provide much better than the mechanical properties of the cement-based material compression, bonding, etc., higher early strength. 2, low exothermic peak: it can provide up to 120 minutes (25 ℃) of operating time, suitable for large volume use grout 3, no shrinkage: ensure that the final shape of the grout layer in full contact with the bearing surface, ensure the installation of high-precision equipment degrees. 4, excellent creep resistance: Epoxy grout can be a long time in -50 ℃ to + 80 ℃ alternately freezing and thawing, vibration compression harsh physical conditions of long-term use without plastic deformation, to ensure long-term accurate positioning equipment. 5, excellent toughness: Epoxy grout can be resolved by the moving device to transmit any possible cement-based grout layer burst dynamic load. 6, corrosion resistance: can withstand acid, alkali, salt, oil and other chemicals, long-term contact corrosion. Second, the application 1, the second filling installation of compressors, pumps, punching machine, grinder, ball mill, high-vibration equipment. 2, susceptible to chemical attack of equipment foundation grouting area. 3, track foundation, bridges and other supporting base area by the strong pressure grouting. 4, bolts, rebar planting and structural concrete construction reinforcement. 5, concrete, stone, steel, wood and other surfaces as a self-leveling mortar use. 6, iron, iron rods, rod steel connections. Third, performance indicators physical performance range (A + B): C≈1: 4 (in line with ASTM Standard) physical properties criterion 1 day 3 days 7 days final compressive strength GB / T50081-2002> 50MPa> 65MPa> 95MPa> 100MPa flexural strength GB / T50081-2002> 10MPa> 15MPa> 20MPa> 25MPa pullout strength GB / T50081-2002> 8MPa> 12MPa> 15MPa> 17MPa compression elastic membrane GB / T50081-2002 / /> 18000MPa> 18500MPa linear shrinkage rate HG / T2625-94 / / <0.012% <0.012% exothermic peak HG / T2625-94 <42 ℃ compression creep GBJ82-85 <1.0 * 10-3mm / mm (180 days) the thermal expansion coefficient GBJ119-88 < 40 * 10-6mm / mm / ℃ (forming 28 days, 0-60 ℃ range test) Note: 1, preheating, molding and curing at 23 ± 2 ℃, relative humidity of 50 ± 5% under experimental conditions, other conditions accordance with the appropriate standards. 2, final data at 23 ± 2 ℃ molding and curing 7 days, then accelerated curing at 60 ℃ 6 hours measured. Fourth, the storage package 1, epoxy grout at room temperature, dry conditions can be stored for at least 18 months. 2, according to Mix Package A: B: C = 25: 10: 150 Fifth, the construction process 1, ready contact with the concrete surface EGM-100 shall be chiseled its surface laitance and expose solid grassroots level, to ensure the grout surface clean and dry and free of grease. Concrete joints grind the outer edge of the 25mm thick bevelled edges to increase the edge of the grout and adhesive base area; and the need to stick metal surface should be free of corrosion (up to SSPC-SP6 finish on request). 2, molding template to be solid, solid lap, its inside with grease, wax or paste PVC tape in order to release; for ease of installation dumping and filling funnel, filling side between the template and equipment around the base to allow at least 100mm distance, and more than 100mm above the equipment chassis. Nailed a 45 ° angle 25mm thick moldings on the inside of the filling level height template to avoid pouring body edge stress concentration. 3, the construction includes a surface temperature of the ambient temperature and air temperature. In order to obtain the best working condition, preferably before filling material is placed for 24 hours at 15-25 ℃ environment; construction and subsequent control within 24 hours ambient temperature 5-32 ℃, 20 ℃ most suitable. Summer construction to avoid the midday heat, when necessary, to build awning; winter temperature is low, should be raised to build greenhouses in the filling area, to ensure that environmental temperature is greater than 5 ℃, the construction should choose noon. 4. Mix 1) with a hand-held blender (200-250rpm) fully mix A (resin), B (hardener) for about 3 minutes; 2) high power at low speed mixer (15-20rpm) was added C (filler) so with A, B mixture was mixed, stir to aggregate all of infiltration is complete, about 5-10 minutes; 3) at low temperatures in order to ensure the flow of the mixture may be appropriate to reduce C (filler) Amount ( Up to 1/2 of the material can be reduced). 5, filling 1) filling grout should be side to side; grouting process can squeeze but do not vibrating, in order to avoid inclusion of air trapping therein; grouting distance is greater than 1.5m, use high filling funnel method, the use of heavy beat heterodyne principle assist grout. Grout work must be completed as soon as continuous; 2) control the thickness of a single grout between 25mm to 350mm, when filling area over 1.8m × 1.8m need to grout locale stretch & n, bsp; contraction joints reserve strip; a single bolt hole filling depth of up to 1500mm. 6. After checking dense grout with a hammer percussion device substrate: Issue tinkle show grout layer of dense, emit sound show grout layer hollowing pound. 7, surface collection of light and form removal after grouting and before EG100 initial setting, to achieve the aesthetic effect, the exposed surface of the received light gray knife; after the final setting, you can form removal. After construction is completed, available water or solvent cleaning grout tool. Initial setting: When 18 ℃, 3hr; 25 ℃ when, 2hr; 32 ℃ when, 1.5hr final setting: When 18 ℃, 72hr; 25 ℃ when, 48hr; 32 ℃ when, 36hr 8, Construction Safety resin portion of the product low toxicity formulation, but there is still a slight irritation, should be used to avoid inhalation of vapors or prolonged contact with the skin; note wear necessary protective equipment to use and keep the environment ventilation should be washed after contact with the skin, such as a splash in the eyes immediately with flush with water.